Non-stick coating system with PTFE-FEP for concentration gradient

ABSTRACT

Improved non-stick coating systems can be applied to untreated smooth substrate with a primer of polytetrafluoroethylene and a perfluorinated copolymer of tetrafluoroethylene and hexafluoropropylene to give a concentration gradient.

BACKGROUND OF THE INVENTION

This invention relates to coatings systems, such as for cookware, which minimize sticking. More particularly, it relates to multilayer coating systems that can be used directly on smooth, untreated substrates and which provide concentration gradients within the coating.

Generally in the art a metal or glass substrate is roughened by some means before the first layer of coating is applied so that mechanical bonding will assist chemical adhesive means in holding the coating onto the substrate. Typical roughening means include acid etching, sand-blasting, grit-blasting, and baking a rough layer of glass, ceramic or enamel frit onto the substrate. The problem of adhesion of non-stick coatings to substrates is exacerbated by the nature of the coatings. If the coating is optimized for release to prevent food particles from sticking to it, for easy clean-up after cooking or durability, or to facilitate low friction sliding contact, almost by definition there will be difficulties in making it adhere well to the substrate.

The substrate can be metal, often aluminum or stainless steel used for cookware or industrial applications. It can be glass or ceramic. It might even be plastic for microwave oven cookware, or it could be an industrial article such as a saw made of carbon steel. Whatever the substrate or the application, if it is necessary to roughen the substrate to make the coating adhere, that at least adds cost and can cause other difficulties including creating a rough profile which can protrude or telegraph through the coating. This is especially undesirable when smoothness is sought, such as for saws, steam irons and copier rolls. The environmental cost of disposing of etchant materials can be significant. Sometimes, especially for glass and ceramic substrates, it also can cause unacceptable weakness or brittleness of the substrate.

Means of enhancing adhesion of non-stick coatings to a substrate are illustrated by the following patents.

U.S. Pat. No. 4,049,863--Vassiliou (1977) teaches a primer containing fluoropolymer, such as polytetrafluoroethylene (PTFE), colloidal silica and a polyamide imide (PAI), along with other constituents, applied by various techniques to a substrate that is preferably pretreated by grit blasting, flame spraying of metals or metal oxides or frit coating, or to phosphated and chromated metals. The PTFE:PAI ratio can be 1:9. The primer coat is ordinarily applied to a dry film thickness (DFT) of about 2-15 microns (μm). After air drying, the primer is topcoated with a conventional fluoropolymer enamel and baked. (Parts, percentages and proportions herein are by weight except where indicated otherwise.)

U.S. Pat. No. 4,087,394--Concannon (1987) discloses aqueous concentration gradient coatings of fluoropolymer which is 20-80% of a homopolymer or a copolymer of fluorinated ethylene-propylene (FEP) made of 5-100% tetrafluoroethylene (TFE) with 95-0% hexafluoropropylene (HFP), with 80-20% of a film forming polymer which can be PAI. The coating is applied by spraying onto aluminum sheet, or a variety of substrates. Other application techniques are mentioned. Nothing is said about substrate preparation. Although PTFE and FEP are treated as a continuum, there are no suggestions to use a blend such as 50% PTFE, 50% FEP.

Representative of nonaqueous perfluoropolymer concentration gradient patents are U.S. Pat. Nos. 3,661,831 (1972) and 4,143,204 (1979) on FEP (preferably 3-20% HFP, balance TFE) with various film formers including PAI. At the end of each specification, example 24 teaches using such a coating as a primer under an ordinary PTFE topcoat on a frypan. U.K. 1,230,339 (1971) claims articles coated with nonaqueous PTFE-PAI with a concentration gradient. This and equivalent Canadian 887,122--Fang (1971) provide a single coating of PAI and PTFE on a metal substrate with a concentration gradient from mostly PAI at the substrate to mostly PTFE at the air interface. This is applied as a single coat without any special primer on ordinary steel or sand-blasted aluminum.

A mixture of FEP and PTFE in an organic dispersion is in U.S. Pat. No. 3,904,575 (1975)--Satokawa. This says that lower molecular weight PTFE permits more FEP to be included in a stable dispersion. The use of PAI and other film formers is also disclosed. The examples teach sand blasting an aluminum substrate before applying the coating.

Also, U.K. 1,454,255--Berghmans and Seymus (1976) discloses aqueous dispersion coatings of mixtures of PTFE and FEP with SiO₂ and aluminum phosphate applied preferably to grit-blasted or frit-coated aluminum, but also specifically to untreated aluminum.

U.S. Pat. No. 4,287,112--Berghmans (1981) discloses PPS with PTFE, FEP and/or a copolymer of tetrafluoroethylene and hydrocarbon ether monomer which have been completely substituted with fluorine atoms as described in U.S. Pat. Nos. 4,292,859 (1981) and 4,351,883 (1982)--both Concannon, known as PFA, along with Al flake and TiO₂ pigment, in both aqueous and non-aqueous coatings. The preferred PTFE is irradiated micropowder. PTFE micropowder may be made according to the teachings of U.S. Pat. Nos. 3,116,226--Bowers (1963), 4,029,890--Brown et al (1977) or 4,200,551--Derbyshire (1980).

Coatings systems including intermediate and top coats useful with the present invention are described in various patents including:

U.S. Pat. No. 4,049,863--Vassiliou (1977);

U.S. Pat. No. 4,118,537--Vary and Vassiliou (1978);

U.S. Pat. No. 4,123,401--Berghmans and Vary (1978);

U.S. Pat. No. 4,252,859--Concannon and Vary (1981);

U.S. Pat. No. 4,351,882--Concannon (1982);

all incorporated herein by reference.

SUMMARY OF THE INVENTION

The present invention, in certain of its embodiments, provides a coating system comprising a substrate with a multi-layer non-stick coating, comprising a primer, a topcoat, and up to one or more intermediate coats between the primer and the topcoat, wherein:

the substrate is free of contaminants that would prevent adhesion of the coating,

the primer is applied to the substrate in the form of an aqueous dispersion comprising perfluorocarbon resin and at least one of polyamide imide, polyarylene sulfide and polyether sulfone resins wherein the perfluorocarbon resin comprises 50-90% by weight of a first resin of polytetrafluoroethylene having a melt viscosity of at least about 10¹⁰ poises plus 50-10% of a second resin of perfluorinated copolymer of hexafluoropropylene and tetrafluoroethylene having a melt viscosity in the range of 10³ to 10⁸ poises, and

the topcoat and any intermediate coats comprise perfluorocarbon resin.

DETAILED DESCRIPTION

The present invention permits not only lower cost by avoiding the roughening of the substrate but also smoother coated surfaces which can be advantageous for release on cookware, and for the gliding effect on steam iron sole plates. Also it can allow elimination of costly polishing of coated copier roll surfaces and application of dispersion PTFE coatings by coil coating and roller coating techniques.

The adhesion of high melt viscosity fluoropolymer coatings to all types of metal substrates, particularly to smooth metal, can be significantly improved through chemically induced stratification or formation of a concentration gradient in the primer. Addition of perfluorocarbon polymer having a melt viscosity (MV) in the range of 10³ -10⁸ poise, to a primer system composed of PTFE (MV=10¹¹) and a polymeric binder such as polyamide-imide or polyphenylene sulfide, imparts a synergistic effect in which the fluoropolymer stratifies away from the substrate interface allowing the polymeric binder to obtain a higher concentration and degree of cure at the substrate interface resulting in improved adhesion. The required cure temperature to achieve this stratification can be modified by the choice of fluoropolymer.

With use of the coatings of the invention on smooth substrates, treated only by washing to remove grease and any other contaminants which might interfere with adhesion, coating systems of the invention give good food release and good resistance to usual durability tests such as the "tiger paw" abuse cooking tests involving a weighted holder with multiple ball point pen shafts rotating around the inside of a frying pan during cooking tests. The tests are generally described in U.S. Pat. No. 4,252,859, col. 2, lines 14-24.

Typical prior art preparation of surfaces to enhance adhesion of a release coating has involved etching or sand or grit blasting to develop a surface profile. The profile is measured in average microinches using a model RT 60 surface roughness tester made by Alpa Co. of Milan, Italy. The profile on typical rolled aluminum after washing to remove grease and contaminants is 16-24 microinches. The profile on steel varies more widely but is typically less than 50 microinches. On both steel and aluminum, before a release coating is applied the profile typically is increased to over 100 micro inches, preferably for aluminum for some uses to 180-220 micro inches. Thus, the present invention is particularly useful with steel or aluminum substrates having a profile of less than 100, preferably less than 50 micro inches.

The primers of the invention can also be used on substrates roughened in various ways known in the art to make coating systems even better than without such undercoats. This can combine improved chemical adhesion with mechanical effects to produce products that may be superior.

In the following examples, the polyamide imide, colloidal silica and dispersions preferably are those of U.S. Pat. No. 4,049,863--Vassiliou (1977); the ultramarine blue is that of U.S. Pat. No. 4,425,448--Concannon and Rummel (1984); the polyether sulfone is that of U.S. Pat. Nos. 3,981,945 (1976), 4,090,993 (1978) --both Atwood et al, and 4,131,711 (1978)--Atwood, and the polyarylene sulfide is the polyphenylene sulfide of U.S. Pat. No. 4,287,112 (1981)--Berghmans.

The following examples and test data demonstrate this improved adhesion when used as a primer for fluoropolymer topcoats. The fluoropolymers are provided as 60% dispersions in water. The compositions were blended by techniques normal in the art and them applied to a smooth, degreased aluminum substrate by spraying.

EXAMPLE 1 FEP/PTFE--Multiple Coat System

                  TABLE 1                                                          ______________________________________                                         Composition: 40% FEP/60% PTFE Primer                                           Weight                                                                         Percent                                                                        ______________________________________                                         0.007     Zinc oxide                                                           0.050     "Afflair 153" titania coated                                                   mica from EM Industries                                              6.497     Ultramarine Blue pigment                                             6.750     "T-30" PTFE from Du Pont                                             0.972     "Ludox AM" colloidal silica from Du Pont                             4.153     "TE9075" FEP from Du Pont                                            4.641     AI-10 polyamide imide resin from Amoco                               67.628    Deionized water                                                      0.630     "Triton X-100" octyl phenol polyether alcohol                                  non-ionic surfactant from Rohm and Haas                              0.655     Diethylethanolamine                                                  1.309     Triethylamine                                                        3.614     Furfuryl alcohol                                                     100.00    TOTAL                                                                ______________________________________                                    

                  TABLE 2                                                          ______________________________________                                         Topcoat                                                                        Weight                                                                         Percent                                                                        ______________________________________                                         0.790     "Afflair 153"                                                        0.389     Channel black pigment                                                0.172     Ultramarine blue pigment                                             0.195     Aluminum silicate                                                    40.704    "T-30" PTFE                                                          0.442     Cerium octoate                                                       0.054     Sodium polynaphthalene sulfonate                                     1.834     Diethylene glycol monobutylether                                     0.928     Oleic acid                                                           33.772    Deionized water                                                      3.480     Triethanol amine                                                     2.246     Hydrocarbon solvent                                                  2.914     "Triton X-100"                                                       12.080    Acrylic latex of 39 parts by weight                                            terpolymer of methyl methacrylate/57 parts                                     ethyl acrylate/4 parts methacrylic acid,                                       dispersion at 40% solids in water, 0.2 μm                                   average particle size                                                100.000   TOTAL                                                                ______________________________________                                    

Application

This system is comprised of a primer of PTFE, FEP and polyamide imide which is applied at 5-10 μm dry film thickness (DFT) to a metal surface which has been washed to remove oil and dirt contamination, air dried, and topcoated with a single (15-17.5 μm DFT) or multiple topcoats in thicknesses 12.5-17.5 μm DFT each and having compositions similar to those shown in Table 2. The films are baked 10 minutes at 150° C. followed by a high temperature bake for a minimum of 3 minutes over 415° C.

Testing

After application of a single layer coating on smooth, degreased 12 gauge aluminum substrate, cured under varying conditions, the coated substrate was soaked in boiling water for 20 minutes. The coating is cut down to the substrate, then a person attempts to pull back the coating with his fingernail. In the following Table, P indicates passing, i.e., the coating did not come loose, failure indicates that it pulled back at least 1 cm.

                  TABLE 3                                                          ______________________________________                                         Fingernail Adhesion on Smooth Aluminum                                         Cure (Temp °C./Time - min)                                              ______________________________________                                         416/3           429/5   432/10                                                 P               P       P                                                      ______________________________________                                    

Tests without the FEP led to failure of this coating.

Two different proportions of FEP and PTFE were used as a primer with a topcoat on smooth aluminum cookware which was subjected to tiger paw testing, described above. The number of standard cooking cycles to a rating of 5, determined by coating deterioration, was recorded and presented below along with the percentages of the comparable value for a commercial coating on a grit-blasted substrate run as a control. The results are better than many good commercial products.

                  TABLE 4                                                          ______________________________________                                         Cooking Performance of FEP/PTFE Primer                                                        Cooks to Rating of 5                                                                                % of                                       System       DFT     Range   Average                                                                               Commercial                                 ______________________________________                                         40% FEP/60% PTFE                                                                            1.0-1.1 80-120   95    114                                        30% FEP/70% PTFE                                                                            1.0-1.1 80-120  103    124                                        ______________________________________                                    

When these coatings are applied as described to smooth degreased cookware aluminum, stainless steel and other metals, they give acceptable crosshatch and fingernail adhesion test results and are as good as or better than a commercial 2-coat system applied to aluminum grit blasted to a profile of 180-220 microinches in terms of release of food, staining, blister resistance in cooking and tiger paw testing.

A preferred topcoat is that of Example 1 of U.S. Pat. No. 4,118,537. Alternatively, the coats above the undercoat and primer (topcoat and optional intermediate coats) can be those of U.S. Pat. Nos. 4,252,854; 4,351,882; and 4,425,448, and combinations thereof. 

I claim:
 1. A coated substrate comprising a substrate with a multi-layer non-stick coating, comprising a primer, a topcoat, and optionally one or more intermediate coats between the primer and the topcoat, wherein:the substrate is free of contaminants that would prevent adhesion of the coating, the primer is applied to the substrate in the form of an aqueous dispersion comprising perfluorocarbon resin and at least one of polyamide imide, and polyether sulfone resins wherein the perfluorocarbon resin comprises 50-90% by weight of a first resin of polytetrafluoroethylene having a melt viscosity of at least about 10¹⁰ poises plus 50-10% of a second resin of perfluorinated copolymer consisting essentially of hexafluoropropylene and tetrafluoroethylene having a melt viscosity in the range of 10³ to 10⁸ poises, and the topcoat and any and all intermediate coats comprise perfluorocarbon resin.
 2. The coated substrate of claim 1 wherein the melt viscosity of said first resin is at least 10¹¹ poises and of said second resin is in the range of 10⁴ -10⁶ poises.
 3. The coated substrate of claim 1 wherein the coating comprises at least one intermediate coat containing the ingredients of the primer.
 4. The coated substrate of claim 1 wherein the substrate is at least one metal selected from the group consisting of aluminum, stainless steel and carbon steel.
 5. The coated substrate of claim 4 wherein the substrate before coating has a surface roughness profile less than 100 micro inches.
 6. The coated substrate of claim 4 wherein the substrate before coating has a surface roughness profile less than 50 micron inches.
 7. The coated substrate of claim 1 wherein the primer contains 3-5% colloidal silica, 1-4% surfactant, 15-30% polyamide imide, and 25-55% perfluoropolymer consisting of 60-85% polytetrafluoroethylene, with balance being the copolymer.
 8. The coated substrate of claim 1 wherein, before application of the primer, the surface of the substrate has been treated to remove contaminants that would interfere with adhesion but has not been etched or mechanically roughened.
 9. The coated substrate of claim 1 wherein the primer coating resulting from said aqueous dispersion is not uniform in composition throughout its thickness but has a lower concentration of polytetrafluoroethylene at the interface with the substrate than at the opposite interface.
 10. A process of making the coating substrate of claim 1 wherein the coatings are applied to the substrate without completely drying one coating before applying the next, and then the entire coating is cured by heating at at least 350° C. 